API-571 API Corrosion and Materials Professional Free Practice Exam Questions (2026 Updated)

API RP 751 (referenced in RP 571) lists materials appropriate for HF acid alkylation service. It specifies:

“Chrome-moly steels such as ASTM A-193 B5 (5% Cr) bolts are preferred for their resistance to HF acid-induced cracking.”

“Standard low alloy steels (e.g., B7) are not considered adequately resistant.”

(Reference: API RP 571 summary & API RP 751, Section 5.6.3 – Bolting Materials)

Therefore, the correct and industry-approved answer is option A.

API RP 571 under Thermal Fatigue highlights:

“Differential thermal expansion between dissimilar materials (e.g., carbon steel and stainless steel) in welds causes high cyclic stresses that can result in thermal fatigue cracking.”

“These stresses typically occur during transient thermal cycling such as startup/shutdown operations.”

(Reference: API RP 571, Section 4.2.1.5 – Thermal Fatigue)

Thus, the correct mechanism resulting from differential expansion in bimetallic welds is thermal fatigue, making option B correct.

According to API RP 571, under Naphthenic Acid Corrosion (NAC):

“The most severe corrosion is typically found in areas of high velocity and turbulence, such as at pump around nozzles, transfer lines, elbows, reducers, and orifices.”

“NAC is characterized by uniform thinning and can accelerate significantly where flow-induced erosion is present.”

(Reference: API RP 571, Section 4.3.4.1 – Naphthenic Acid Corrosion)

This clearly establishes that high velocity and turbulence increase NAC severity, making option D correct.